AISI 410 has a high strength and hardness and supplied in a hardened and double tempered condition. It is typically used in the oil and gas market in a wide variety of wellhead applications.
TM Steels can provide all materials produced to bespoke customer requirements. We project manage your raw material or semi finished material requirements, including Sawing, Heat Treatment, Testing, Rough Machining, Hardness Testing, Ultrasonic Examination and certification, including BS EN 10204 3.1 & BS EN 10204 3.1 Witness documentation packages. We use an approved list of European Mills, and can offer material with UKAS accredited Testing. Contact our sales team today if you would like to enquire about our AISI410 Stainless Stock Lines.
|
C |
Si |
Mn |
P |
S |
Cr |
Ni |
Al |
Cu |
Sn |
|
|
Min |
0.12 |
0.15 |
0.4 |
11.5 |
0.3 |
0.015 |
||||
|
Max |
0.15 |
0.4 |
0.6 |
0.015 |
0.01 |
13.5 |
0.5 |
0.035 |
0.25 |
0.1 |
|
Tensile |
Result |
|
RP 0.2% |
80,000 PSI MIN |
|
RM |
100,000 PSI MIN |
|
A 4d |
18% |
|
Z |
35% |
|
HBW10/3000 |
217-237 |
|
KCV @ -29 DEG C |
27J MIN AVE, 20J MIN SINGLE VALUE |
SURFACE CONDITION
Peeled / Smooth Turned Bar.
REDUCTION RATIO
4:1 Min
STRUCTURE
Grain size will be ASTM 5 or finer.
ULTRASONIC EXAMINATION
Ultrasonic examination available per ASTM A388/API6A Latest Edition or to bespoke customer specification.
Rolled/Peeled Bar
Hardened and double tempered to meet 80ksi minimum yield, 22HRc maximum.
25.4mm – 215.9mm ⌀
Forged/Peeled Bar
Hardened and double tempered to meet 80ksi minimum yield, 22HRc maximum.
228.6mm – 406.4mm ⌀
| 410 Stainless | X12Cr13 | 1.4006 | SS 2302 | SUS 410 | BS 410S21 | UNS S41000 | EN 56A |